| TYPICAL VALUES |
 |
Results |
| PROPERTY |
TEST METHOD |
ENGLISH |
METRIC |
|---|
| Thickness Film |
Micrometer |
.02 ± 10% |
.050mm ± 10% |
| Thickness Adhesive |
Micrometer |
.001-.0012 |
.026mm - .032mm |
| Tensilee Strength |
Instron Tensile Tester - jaw separation 2 in. and a speed of 12 in. per min. |
5 lb/in. minimum
73ºF |
.9 kg/cm minimum
23ºC |
| Elongation |
Instron Tensile Tester
(as above) |
100% at 73ºF |
100% minimum |
For all properties given below, film was applied to an acrylic substrate at 73ºF (23ºC) 24 hours before testing.
|
|
Results |
| PROPERTY |
TEST METHOD |
ENGLISH |
METRIC |
|---|
Temperature
Range |
Good adhesion and minimal staining when exposed to any temperature within range specified. |
-20ºF to +175ºF |
-29ºC to 80º°C |
| Adhesion |
180° pullback at 12” (30.5cm) per minute |
4.0 lb/in. |
0.7 kg/cm |
CHEMICAL RESISTANCE
Unless otherwise specified, the film was applied to an acrylic substrate at 73ºF, 23ºC, 24 hours before testing. The samples are immersed in the noted chemical agent at 73ºF, 23ºC, and after testing are wiped clean.
| Chemical Agent |
Exposure Time |
Results |
| Water |
24 hours |
No effect |
| Mild soap and water |
24 hours |
No effect |
| 20% Isopropyl Alcohol/80% water |
10 minutes |
No effect 10% |
| Hydrochloric Acid |
10 minutes |
No effect |
| 10% Ammonium Hydroxide |
10 minutes |
No effect |
| 